coatingli 发表于 2004-6-17 06:38:00

膜系

<img src="data/attachment/forum/dvbbs/2004-6/2004616223744173.bmp" border="0" onload="if(this.width>screen.width*0.7) {this.resized=true; this.width=screen.width*0.7; this.alt=\'Click here to open new window\nCTRL+Mouse wheel to zoom in/out\';}" onmouseover="if(this.width>screen.width*0.7) {this.resized=true; this.width=screen.width*0.7; this.style.cursor=\'hand\'; this.alt=\'Click here to open new window\nCTRL+Mouse wheel to zoom in/out\';}" onclick="if(!this.resized) {return true;} else {window.open(\'data/attachment/forum/dvbbs/2004-6/2004616223744173.bmp\');}" onmousewheel="return imgzoom(this);" alt="" />
TIO2   91.51
SIO2149.38
TIO2   81.24
SIO2139.81
TIO2   80.41
SIO2137.23
TIO2   80.47
SIO2137.06
TIO2   81.23
SIO2139.13
TIO2   83.52
SIO2145.46
TIO2   90.21
SIO2161.23
TIO2   99.02
SIO2162.97
TIO2   94.44
SIO2158.85
TIO2   98.44
SIO2169.88
TIO2103.87
SIO2172.61
TIO2103.89
SIO2170.78
TIO2100.21
SIO2162.89
TIO2   96.51
SIO2163.49
TIO2   99.45
SIO2166.02
TIO2   98.85
SIO2   82.06

yin99 发表于 2004-6-17 21:18:00

yh15430 发表于 2004-6-18 04:09:00

回复：（ahcg）镀不出来，

coatingli：用晶振控还是光控？

zz 发表于 2004-6-18 04:53:00

<P>试镀过没?</P>

zhoucheng 发表于 2004-6-18 05:53:00

<P>可以,我做过相同的</P>

yin99 发表于 2004-6-19 01:08:00

sesame_1978 发表于 2004-6-19 19:57:00

换Ta2O5可以，TiO2在400nm有吸收，T最多到75％左右，我做了很久都不行，听说钛酸镨可以可是一直没有用过这种材料，谁用过，交流一下？

likeoe 发表于 2004-6-20 17:02:00

<P>我也推断coatingli的结果是设计结果，用TiO2哪来的那么好（400以下的）？</P>

heyanch 发表于 2004-6-20 21:48:00

光催化正是利用tio2在400nm以下的强吸收。

jinfeng 发表于 2004-6-21 18:05:00

<P>1.0625L 1.125H0.5625L(0.5LH0.5L)^5 0.55L 1.1H 0.55L</P>

htuwf 发表于 2005-2-21 22:15:00

<P>leybold机器早就可以做出来了</P>

帅的按不住 发表于 2005-2-22 18:05:00

只要机器好就行...............